ANALISIS KEBUTUHAN PEMASANGAN ZINK ANODE UNTUK MENCEGAH KOROSI PADA LAMBUNG KAPAL KAPAL GENERAL CARGO
DOI:
https://doi.org/10.54378/bt.v14i2.402Kata Kunci:
Replacement Sacrificial anodes, corrosion, hull.Abstrak
Needs installation of cathodic protection to prevent corrosion of the ship in the sea water medium is a must so that the ships can be used as long as possible, but the effectiveness is very limited lifespan sacrificial anode that time should be right on time. For the replacement timing becomes important to do, hull plate is first exposed areas of sea water. In this area of the hull bottom water or top area of water exposed to corrosion range. Corrosion of hull plates can lead to decline in strength and service life of ships, reducing the ship's speed and reduce safety and security of cargo and passengers. From the calculation of the aluminum anode needs indicated that there is a difference between the life of the anode replacement is supposed to 5.25 years. The number of victims aluminum anode required to ship the object of the research is based on the calculation is 12 pieces (± 44.2 kg), lower than the number of anode installed in the field about 24 pieces (108 Kg). So the amount of victims aluminum anode mounted on General Cargo Ship in the field is redundant with past-year use of 5.25 while the turn is done for 3 years. For the owners of the ship, you should use zinc or magnesium anode victim since both of these materials have an efficiency of 95 % compared to aluminum, is only 50 %.
Referensi
BKI, 2014, Rules Volume II Section 38.
D. Binkoosky, 2003, Technology of Ship Repairing, Moscow.
Det Norske Veritas (DnV) RP–B401, 2003, Cathodic Protection Design. Oslo.
Hoang Thi Bich Thuy, Phan Luong Cam, 2006, Performance of The Zinc Sacrificial Anode in Concrete Environment, Corrosion and Protection Research Center, Hanoi University of Technology, Vietnam.
James B. Bushman PE, 2007, Galvanic Anode Cathodic Protection System Design, Principal Corrosion Engineer, Bushman and Associates, Inc, Medina, Ohio, USA.
Jinglei Zhang, Gongyu Guo, Keliang Sun, Baorong Hou, 2007, Electrochemical Evaluation of Dissolution Characteristics of All Based Sacrificial Anodes in Seawater, Institute of Oceanology, Academia Sinica, Qingdao.
Kjernsmo Dag, Kleven Kjell, Schele Jan, 2003, Corrosion Protection, Frosio, Denmark.
Suratman Rochim, 2005, Teknologi Perlindungan Logam, Seminar Nasional: Aplikasi Teknologi Perlindungan Logam di Industri, Jurusan Teknik Metalurgi Universitas Jenderal Ahmad Yani Bandung.
Talavera M.A, Valdez S, Juarez-Islas JA, Mena B. Genesca J, 2002, EIS Testing of New Aluminium Sacrificial Anodes, Journal of Applied Electrochemistry, 32: 897–903.
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
PEMBERITAHUAN HAK CIPTA
KEBIJAKAN YANG DIAJUKAN UNTUK JURNAL YANG MENAWARKAN AKSES TERBUKA
Syarat yang harus dipenuhi oleh Penulis sebagai berikut:
- Penulis menyimpan hak cipta dan memberikan jurnal hak penerbitan pertama naskah secara simultan dengan lisensi di bawah Creative Commons Attribution License yang mengizinkan orang lain untuk berbagi pekerjaan dengan sebuah pernyataan kepenulisan pekerjaan dan penerbitan awal di jurnal ini.
- Penulis bisa memasukkan ke dalam penyusunan kontraktual tambahan terpisah untuk distribusi non ekslusif versi kaya terbitan jurnal (contoh: mempostingnya ke repositori institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan penerbitan awalnya di jurnal ini.
- Penulis diizinkan dan didorong untuk mem-posting karya mereka online (contoh: di repositori institusional atau di website mereka) sebelum dan selama proses penyerahan, karena dapat mengarahkan ke pertukaran produktif, seperti halnya sitiran yang lebih awal dan lebih hebat dari karya yang diterbitkan.