ANALISIS SIFAT MEKANIK BAJA SKD 61 DENGAN BAJA ST 41 DILAKUKAN HARDENING DENGAN VARIASI TEMPERATUR

Authors

  • Media Nofri Program Studi Teknik Mesin Institut Sains dan Teknologi Nasional ISTN Jakarta Selatan
  • Acang Taryana

DOI:

https://doi.org/10.54378/bt.v13i2.218

Keywords:

hardening, SKD 61, ST 41.

Abstract

The alloy steel that is widely used in the world of manufacturing industry is the type of tool steel because it has special characteristics and includes special steel. One type of tool steel that is widely used by the manufacturing industry is SKD steel type 61. ST 41 steel material is a low carbon steel with a carbon content of 0.08% -0.20%. ST 41 steel is commonly used as industrial machine component, but in this ST 41 steel is not as strong as steel SKD 61. So, to improve quality to ST 41 steel. Quality improvement can be done by heat treatment process. To obtain hardness requires the heating process, holding time, cooling medium, precise hardening temperature and see the material comparison between SKD 61 steel and ST 41 steel before and after the hardening process to the nature of hardness and microstructure. Result of hardness test of SKD 61 nonheattreatment steel material has hardness value equal to 197 HV, ST 41 nonheatreatment steel material has hardness value equal to 165 HV, after hardening for temperature 900⁰C has hardness value 154 HV, temperature 950⁰C has hardness value 152 HV, temperature 1000⁰C has 161 HV magnification value. Seen in the metallographic results appear to be a change in microstructure on ST 41 steel which after the hardening structure looks more dominant after the hardening structure turned into bainite-ferrit

References

ASM Handbook. 1991. Heat Treating.ASM hanbook Committee. Volume 4. page 17.

Adyana, D.N, Teknologi Manufaktur Logam Industri, ISTN, Jakarta, 2014.

Adi, yeuwono. “Perlakuan Panas Pada Logam Dan Jenisnya”. 04 juni 2011. http://tekno-sehat.blogspot.co.id/2011/06/Perlakuan-Panas-(Heat Treatment)-Pada-Logam-Dan-Jenisnya/

Adnyana D.N., Logam dan Paduan Tinjauan Tentang Proses Pengolahan Dan Hubungan Antar Struktur Dengan Sifat Mekanis, Jakarta, 1978.

Callister, William D, 2007. Mayerial Science and Engineering7. jhon wiley&sons,Inc.kanada

Suherman, W, Perlakuan Panas, ITS, Surabaya, 1991

Adhy Prayitno, Ismet Inonu .Pengaruh Perbedaan Waktu Penahanan Suhu Stabil Terhadap Kekerasan.1999)

Wijono, Djoko. Teori Praktikum Ilmu Logam, LUK-BPP Teknologi, 1994

Susanto, Median Fide(2004), tugas akhir : ”PENGARUH PERLAKUAN PANAS TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO PADA BAJA KARBON RENDAH S 30 C”,Institut Sains dan Teknologi Nasional. Jakarta.

Jhon E.bringas (2004), ”Handbook of comparative Word steel standards”.

Sinaga, Rinto Veni (2014), tugas akhir : ”PENGARUH NITRIDASI PLASMA TERHADAP PERUBAHAN KEKERASAN, STRUKTUR MIKRO BAJA PERKAKAS SKD61 PLUNGER TIP KOMPONEN MESIN HIGH PRESSURE DIE CASTING”. Universitas Mercubuana Jakarta.

http://Perlakuan Panas (Heat Treatment) Pada Logam Dan Jenisnya Tekno-Sehat

Downloads

Published

2017-12-20

Issue

Vol. 13 No. 2 (2017): Bina Teknika

Section

Articles

License

Journal Bina Teknika grants open acces to all of its content, based on that matter makes all research papers published are freely available to public which ensures greater global excchange of knowledge

  Creative Commons License

Journal Bina Teknika is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

Refers to these license, all research papers agree to the following terms:

  • Attribution - Authors holds the credit of their research works published, in order to use materials from one or more research papers published in Bina Teknika should be given appropriate credit
  • Non Commercial - All research papers published in Bina Teknika may not use for commercial purposes
  • Share Alike - Any creation made under one or more concepts from research papers published in Bina Teknika should be distribute your contributions under the same license as original