ANALISIS SIFAT MEKANIK BAJA SKD 61 DENGAN BAJA ST 41 DILAKUKAN HARDENING DENGAN VARIASI TEMPERATUR
DOI:
https://doi.org/10.54378/bt.v13i2.218Kata Kunci:
hardening, SKD 61, ST 41.Abstrak
The alloy steel that is widely used in the world of manufacturing industry is the type of tool steel because it has special characteristics and includes special steel. One type of tool steel that is widely used by the manufacturing industry is SKD steel type 61. ST 41 steel material is a low carbon steel with a carbon content of 0.08% -0.20%. ST 41 steel is commonly used as industrial machine component, but in this ST 41 steel is not as strong as steel SKD 61. So, to improve quality to ST 41 steel. Quality improvement can be done by heat treatment process. To obtain hardness requires the heating process, holding time, cooling medium, precise hardening temperature and see the material comparison between SKD 61 steel and ST 41 steel before and after the hardening process to the nature of hardness and microstructure. Result of hardness test of SKD 61 nonheattreatment steel material has hardness value equal to 197 HV, ST 41 nonheatreatment steel material has hardness value equal to 165 HV, after hardening for temperature 900⁰C has hardness value 154 HV, temperature 950⁰C has hardness value 152 HV, temperature 1000⁰C has 161 HV magnification value. Seen in the metallographic results appear to be a change in microstructure on ST 41 steel which after the hardening structure looks more dominant after the hardening structure turned into bainite-ferritReferensi
ASM Handbook. 1991. Heat Treating.ASM hanbook Committee. Volume 4. page 17.
Adyana, D.N, Teknologi Manufaktur Logam Industri, ISTN, Jakarta, 2014.
Adi, yeuwono. “Perlakuan Panas Pada Logam Dan Jenisnya”. 04 juni 2011. http://tekno-sehat.blogspot.co.id/2011/06/Perlakuan-Panas-(Heat Treatment)-Pada-Logam-Dan-Jenisnya/
Adnyana D.N., Logam dan Paduan Tinjauan Tentang Proses Pengolahan Dan Hubungan Antar Struktur Dengan Sifat Mekanis, Jakarta, 1978.
Callister, William D, 2007. Mayerial Science and Engineering7. jhon wiley&sons,Inc.kanada
Suherman, W, Perlakuan Panas, ITS, Surabaya, 1991
Adhy Prayitno, Ismet Inonu .Pengaruh Perbedaan Waktu Penahanan Suhu Stabil Terhadap Kekerasan.1999)
Wijono, Djoko. Teori Praktikum Ilmu Logam, LUK-BPP Teknologi, 1994
Susanto, Median Fide(2004), tugas akhir : ”PENGARUH PERLAKUAN PANAS TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO PADA BAJA KARBON RENDAH S 30 C”,Institut Sains dan Teknologi Nasional. Jakarta.
Jhon E.bringas (2004), ”Handbook of comparative Word steel standards”.
Sinaga, Rinto Veni (2014), tugas akhir : ”PENGARUH NITRIDASI PLASMA TERHADAP PERUBAHAN KEKERASAN, STRUKTUR MIKRO BAJA PERKAKAS SKD61 PLUNGER TIP KOMPONEN MESIN HIGH PRESSURE DIE CASTING”. Universitas Mercubuana Jakarta.
http://Perlakuan Panas (Heat Treatment) Pada Logam Dan Jenisnya Tekno-Sehat
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
PEMBERITAHUAN HAK CIPTA
KEBIJAKAN YANG DIAJUKAN UNTUK JURNAL YANG MENAWARKAN AKSES TERBUKA
Syarat yang harus dipenuhi oleh Penulis sebagai berikut:
- Penulis menyimpan hak cipta dan memberikan jurnal hak penerbitan pertama naskah secara simultan dengan lisensi di bawah Creative Commons Attribution License yang mengizinkan orang lain untuk berbagi pekerjaan dengan sebuah pernyataan kepenulisan pekerjaan dan penerbitan awal di jurnal ini.
- Penulis bisa memasukkan ke dalam penyusunan kontraktual tambahan terpisah untuk distribusi non ekslusif versi kaya terbitan jurnal (contoh: mempostingnya ke repositori institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan penerbitan awalnya di jurnal ini.
- Penulis diizinkan dan didorong untuk mem-posting karya mereka online (contoh: di repositori institusional atau di website mereka) sebelum dan selama proses penyerahan, karena dapat mengarahkan ke pertukaran produktif, seperti halnya sitiran yang lebih awal dan lebih hebat dari karya yang diterbitkan.