PENGARUH MEDIA PENDINGIN TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PLAT BAJA KARBON ASTM A-36
DOI:
https://doi.org/10.54378/bt.v11i2.108Keywords:
Microstructure, DiaustenisationAbstract
working. Workmanship of austenisation is done through warm-up of specimen at temperature 9000C during one hour clock, then made cool in coolant giving speed of different refrigeration. As coolant is refrigeration of lag in refrigeration stove in air-gap (air), dye oli, and dye water giving speed of highest refrigeration. Attempt result indicate that strength of steel from material early 423,9 MPa, after diaustenisation specimen, the strength increase becoming 474,9 MPa through air cooling, and 560,5 MPa through refrigeration dye water. Media cooler dye water, yield mechanical property is less good, because specimen manjadi is fragible (small elongation 6%). Microstructure observation becomeed militant, phase which formed is ferrite as matrik and pearlite. Increasing of strength of call is caused by item formed by pearlite is higher distribution from at initial material. Specimen with refrigeration dye water, microstructure type which formed becoming change, phase which formed is ferrite of form of needle as matrik and martensite. This microstructure type give metal become brittle. Although the strength is highest (717,3 MPa).References
ASTM. Metal Hand Book, “Properties and Selection Iron and Steel” 9th ed, vol 1, Formely Tenth Edition Metal Hand Book, Second Printing, 1992.
Annual Book of ASTM Standard, Section 3, Metal Test Methods and Analytical Prosedures, ”Metals-Mechanical Testing”, Eleveted and low Temperatur Test, Metallography, Vol.03.01.
B.Zakharov, “Heat Treatment of Metals”, Peace Publisher, Moscow.
George E. Dieter, “Mechanical Metallurgy”, International Student Edition, Second Edition Mc.Graw-Hill Kogakusha Ltd, Tokyo, 1978.
George E. Dieter, “Work Ability Testing Techniquues”, ASM, Metal Park Ohio 44073, 1984.
George Krauss, “Heat Treatment and Processing Principle”, Material Park, Ohio 44073.
Herman W.pollack, “Materials Sciece and Metalurgi”, Third Edition, Reston Publishing Company, Inc.
K-E Thelning, “Steel and Its Heat Treatment, Bofors Handbook, 1974.
Marder, A,R,”The Effect of Heat Treatment on The Properties”, Metal Trans, Vol 12A, Sep. 1981.
Downloads
Published
Issue
Section
License
Journal Bina Teknika grants open acces to all of its content, based on that matter makes all research papers published are freely available to public which ensures greater global excchange of knowledge
Journal Bina Teknika is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
Refers to these license, all research papers agree to the following terms:
- Attribution - Authors holds the credit of their research works published, in order to use materials from one or more research papers published in Bina Teknika should be given appropriate credit
- Non Commercial - All research papers published in Bina Teknika may not use for commercial purposes
- Share Alike - Any creation made under one or more concepts from research papers published in Bina Teknika should be distribute your contributions under the same license as original